| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 流动系数 | 260℃,3.8kg | ASTM D1238 | 13 | g/10min |
| 成型收缩率 | ASTM D955 | 0.4-0.6 | % | ||
| 螺旋流动长度 | 260℃,2×4.8mm | CHIMEI | 98 | mm | |
| 吸水率 | 23℃,24hrs | ASTM D570 | 0.4 | % | |
| 比重 | ASTM D792 | 1.13 | |||
| 机械性能 | 弯曲模量 | 23℃ | ASTM D790 | 23000 | kg/cm2 |
| Izod缺口冲击强度 | 1/8″ | ASTM D256 | 55 | Kg.cm/cm | |
| 延伸率 | 23℃ | ASTM D638 | 85 | % | |
| 引张强度 | 23℃ | ASTM D638 | 540 | kg/cm2 | |
| 弯曲强度 | 23℃ | ASTM D790 | 800 | kg/cm2 | |
| 热性能 | 阻燃性 | UL94 | HB | ||
| 线膨胀系数 | 40-100℃ | ASTM D696 | 6-8 | ×105cm/cm/℃ | |
| 软化点温度 | ASTM D1525 | 136 | ℃ | ||
| 热变形温度 | 未退火,1.82MPa | ASTM D648 | 106 | ℃ |
|